Elektryczny żelazko spawanie drut końcówki i spawanie niezbędne
Ręczny proces:
1. Sprawdź przed operacja
(1) Wstaw the electric soldering iron plug into the specified socket 3-5 minutes before welding, and check whether the soldering iron is hot. If it is not hot, first check whether the socket is plugged in. Report, do not disassemble the soldering iron at will, let alone directly touch the solder iron tip with your hands.
(2) The soldering iron tip that has been oxidized and uneven or with a hook should be updated: 1. It can ensure good heat conduction effect; 2. Ensure the quality of the soldered object. If a new soldering iron tip is replaced, the maintenance paint should be wiped off after heating, and tin maintenance should be added immediately. The cleaning of the soldering iron should be carried out before the soldering operation. If the soldering iron is not used for more than 5 minutes, the power must be turned off. The sponge needs to be cleaned. Dirty sponges contain metal particles, or sponges containing sulfur will damage the tip of the soldering iron. 3) Check whether the tin-absorbing sponge has water and is clean. If there is no water, please add an appropriate amount of water (the appropriate amount means that water seeps out when the sponge is pressed to half the thickness of the normal state. The specific operation is: humidity requirements After the sponge is completely wet, Hold it in the palm of your hand and close your five fingers together naturally), the sponge should be cleaned, as dirty sponges contain metal particles, or sponges containing sulfur will damage the tip of the soldering iron.
(4) Whether the human body and the solder iron are reliable grounded, and whether the human body wears an electrostatic ring.
2. Spawanie kroki
A specyficzne operacja kroki z żelazo spawanie może być podzielone na pięć kroki, który jest wywołany pięciokrokowy inżynieria metoda. Do uzyskać dobry spawanie jakość, it must be strictly operated as pokazano in Rysunek 5.
Lutowanie zgodnie z do powyżej kroki jest jeden z do uzyskać dobry lut złącza. W rzeczywiste produkcja% 2c najbardziej prawdopodobne naruszenie z operacji kroki jest to żelazo końcówka nie w kontakt z spawany część pierwszy % 2c ale z lut drut pierwszy, i stopiony lut krople na nie podgrzewany część do być spawany. W ten sposób , to jest łatwy do przyczyna fałsz spawanie z z lut złącza, tak końcówka żelazo musi być w kontakcie z przedmiotem obrabianym do być spawane. podgrzewanie przedmiot obrabiany do być spawany jest ważny środki do zapobieganie fałsz spawanie.
3. Welding essentials
(1) The contact mode between the soldering iron tip and the two parts to be welded (as shown in Figure 6)
Contact position: The soldering iron tip should be in contact with the two welded parts (such as solder feet and pads) to be connected at the same time. The soldering iron is generally inclined at 45 degrees, and should avoid contacting only one of the welded parts. When the heat capacity of the two welded parts is very different, the inclination angle of the soldering iron should be adjusted appropriately. The smaller the inclination angle between the soldering iron and the welding surface, the larger the contact area between the welded part with the larger heat capacity and the soldering iron will be, and the heat conduction capacity will be enhanced. For example, the inclination angle of LCD pull welding is about 30 degrees, and the inclination angle of welding microphones, motors, speakers, etc. can be about 40 degrees. Two parts to be welded can reach the same temperature in the same time, which is considered as an ideal state of heating.
Kontakt ciśnienie: Kiedy żelazo końcówka jest w kontakt z przedmiot obrabiany do być spawany, a lekki nacisk powinien być zastosowany. Wytrzymałość z ciepło przewodnictwo jest proporcjonalny do zastosowany ciśnienie, ale zasada jest nie przyczyna uszkodzenie do powierzchni z spawanego kawałka.
(2) Dostawa metoda spawanie drut
Dostawa czas% 3a W zasada, lut lut drut jest natychmiast kiedy temperatura z spawania osiąga temperatura z lutu lutownego.
Podaż pozycja: To powinno być pomiędzy żelazo i spawane część oraz jako blisko to pad jak możliwe.
Dostawa ilość: To zależy na rozmiar z spawania i podkładka. Po lut pokrywa podkładka, lut można być wyższa niż 1/3 z średnica podkładka podkładka.
(3) Welding time and temperature setting
A. The temperature is determined by the actual use. It is most suitable to solder a solder point for 4 seconds, and the maximum is no more than 8 seconds. Zwykle obserwować the tip of the solder iron. When it turns purple, the temperature setting is is too high.
B. Dla ogólne in-line elektroniczne materiały, set the actual temperature of the solder iron tip to (350~370 degrees); for surface mount materials (SMC), set the actual temperature of the solder iron tip to (330~350 degrees)
C. For special materials, the temperature of the soldering iron needs to be specially set. FPC, LCD connectors, etc. should use silver-containing tin wire, and the temperature is generally between 290 degrees and 310 degrees.
D. Kiedy duże komponentowe stopy, temperatura powinno nie przekraczać 380 stopnie, ale ty możesz zwiększyć moc z żelazo.
(4) Precautions for welding
A. Przed spawanie% 2c obserwować czy każdy lut połączenie (miedź skóra) jest gładki i utleniony.
B. Kiedy spawanie elementy, be sure to look at the welding point to avoid short circuitd caused by poor welding of the line
4. Check after operation:
(1) Po użyciu żelazo, wycieranie off the remaining tin on the tip of the soldering iron with a sponge.
(2) After get off work every day, the tin beads, tin slag, dust, etc. on the soldering iron stand must be cleaned, and then the soldering iron is placed on the soldering iron stand.
(3) Put the cleaned electric solder solder iron on the upper right corner of the workbench.